Synthesis and Physical Properties of Non-Crystalline Nylon 6 Containing Dimer Acid

In this study, a long carbon chain dimer acid is introduced into a nylon 6 structure and is copolymerized with different structural amines to produce amorphous nylon 6 by 4,4'-methylenebis(2-methylcyclohexylamine) (MMCA) in different copolymerization ratios. The effect of different structures and copolymerization ratios on the properties of nylon 6 is determined, along with the thermal properties, crystallinity, water absorption, dynamic mechanical properties, and optical properties. It is found that the melting point and the thermal cracking temperature Td10 of nylon 6 are respectively between 176 °C and 213 °C and 378 °C to 405 °C. The effect of introducing a bicyclohexane group containing a methyl side chain is greater than that of a meta-benzene ring, so COMM (synthesized by Caprolactam (C), dimer oleic acid (OA), and 4,4'-Methylenebis(2-methylcyclohexylamine) (MMCA)) has the lowest melting point, enthalpy, and crystallinity. As the copolymerization ratio increases, its thermal properties decrease. 10% is the lowest crystallinity. The amine structure containing a bicycloalkyl group has lower water absorption and a 10% copolymerization ratio gives the lowest water absorption. It contains the bicycloalkyl group, COM (synthesized by Caprolactam (C), dimer oleic acid (OA) and 4,4'-Methylenebis(cyclohexylamine) (MCA)), which has the highest loss modulus. The lowest loss modulus is noted for a copolymerization ratio of 7% and the value of tan δ increases as the copolymerization ratio increases. The introduction of nylon 6 with the bicycloalkyl groups, COMM and COM, significantly increases transparency. As the copolymerization ratio increases, the transparency increases and the haze decreases. The best optical properties are achieved for 10% copolymerization.