Fabrication of Ultrafine PPS Fibers with High Strength and Tenacity via Melt Electrospinning

Zuo-Ze Fan1, Hong-Wei He2, Xu Yan3

  • 1Industrial Research Institute of Nonwovens & Technical Textiles, College of Textiles & Clothing, Qingdao University, Qingdao 266071, China. 2017021409@qdu.edu.cn.

Polymers
|April 10, 2019
PubMed

Keywords:
PPS fibershigh tensile ductilityhigh-performance fibersmelt electrospinning

More Related Videos

Fabrication of Small Caliber Stent-grafts Using Electrospinning and Balloon Expandable Bare Metal Stents06:55

Fabrication of Small Caliber Stent-grafts Using Electrospinning and Balloon Expandable Bare Metal Stents

Published on: October 26, 2016

9.4K
Fabrication and Characterization of Griffithsin-modified Fiber Scaffolds for Prevention of Sexually Transmitted Infections12:21

Fabrication and Characterization of Griffithsin-modified Fiber Scaffolds for Prevention of Sexually Transmitted Infections

Published on: October 31, 2017

7.9K

Related Concept Videos

Comparing Intermolecular Forces: Melting Point, Boiling Point, and Miscibility02:34

Comparing Intermolecular Forces: Melting Point, Boiling Point, and Miscibility

Intermolecular forces are attractive forces that exist between molecules. They dictate several bulk properties, such as melting points, boiling points, and solubilities (miscibilities) of substances. Molar mass, molecular shape, and polarity affect the strength of different intermolecular forces, which influence the magnitude of physical properties across a family of molecules.
Temporary attractive forces like dispersion are present in all molecules, whether they are polar or nonpolar. They...
51.1K
Phase Transitions: Melting and Freezing02:39

Phase Transitions: Melting and Freezing

Heating a crystalline solid increases the average energy of its atoms, molecules, or ions, and the solid gets hotter. At some point, the added energy becomes large enough to partially overcome the forces holding the molecules or ions of the solid in their fixed positions, and the solid begins the process of transitioning to the liquid state or melting. At this point, the temperature of the solid stops rising, despite the continual input of heat, and it remains constant until all of the solid is...
14.8K
Acid Strength and Molecular Structure03:05

Acid Strength and Molecular Structure

Binary Acids and Bases
In the absence of any leveling effect, the acid strength of binary compounds of hydrogen with nonmetals (A) increases as the H-A bond strength decreases down a group in the periodic table. For group 17, the order of increasing acidity is HF < HCl < HBr < HI. Likewise, for group 16, the order of increasing acid strength is H2O < H2S < H2Se < H2Te. Across a row in the periodic table, the acid strength of binary hydrogen compounds increases with increasing...
32.9K
Strength of Cement01:20

Strength of Cement

Strength tests for cement are not performed directly on neat cement paste due to difficulty in obtaining consistent, reliable specimens. Instead, cement is typically tested in the form of cement-sand mortar.
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in...
482
Relation Between Tensile Strength and Compressive Strength of Concrete01:30

Relation Between Tensile Strength and Compressive Strength of Concrete

Concrete is a fundamental building material, and understanding its strengths is crucial for construction projects. The relationship between its tensile and compressive strengths is intricate, showing that while these strengths are related, they do not increase at the same rate. Tensile strength's growth is slower and is affected by various factors such as the methods used for testing, the size and shape of the specimen, the texture of the aggregate used, and the moisture content of the...
667
The Equilibrium Binding Constant and Binding Strength02:18

The Equilibrium Binding Constant and Binding Strength

The equilibrium binding constant (Kb) quantifies the strength of a protein-ligand interaction. Kb can be calculated as follows when the reaction is at equilibrium:
14.9K