Cellulose Nanofiber/Carbon Nanotube Conductive Nano-Network as a Reinforcement Template for Polydimethylsiloxane...

Both cellulose nanofiber (CNF) and carbon nanotube (CNT) are nanoscale fibers that have shown reinforcing effects in polymer composites. It's worth noting that CNF and CNT could form a three-dimensional nano-network via mixing and vacuum filtration, which exhibit excellent mechanical strength and electrical conductivity. In this study, the developed CNF/CNT film was applied as a nano-network template and immersed into polydimethylsiloxane (PDMS) solutions. By controlling the immersed polydimethylsiloxane pre-polymer concentration, the PDMS/CNF/CNT nanocomposite with various PDMS contents were fabricated after a curing process. Morphological images showed that the CNF/CNT nano-network was well-preserved inside the PDMS, which resulted in significantly improved mechanical strength. While increasing the PDMS content (~71.3 wt %) gave rise to decreased tensile strength, the PDMS-30/CNF/CNT showed a fracture strain of 7.5%, which was around seven fold higher than the rigid CNF/CNT and still kept a desirable strength-Young's modulus and conductivity of 18.3 MPa, 805 MPa, and 0.8 S/cm, respectively. Therefore, with the enhanced mechanical properties and the electrical conductivity, the prepared PDMS/CNF/CNT composite films may offer promising and broad prospects in the field of flexible devices.