The In Vitro Enzymatic Degradation of Cross-Linked Poly(trimethylene carbonate) Networks

The in vitro enzymatic degradation of cross-linked poly(trimethylene carbonate) networks (PTMC-Ns) was performed in lipase solutions at 37 °C, and the effect of the initial molecular weight and cross-linker amount as well as the cross-linker type on the degradation rate of PTMC-Ns was investigated. Due to their denser structure and more hydrophobic surface as well as the higher glass transition temperature, a slower degradation rate was seen for PTMC-Ns with high initial molecular weight at a given cross-linker amount. Similar results could be observed as the cross-linker amount increased, and cross-linker type also influenced the degradation rate of PTMC-Ns. Furthermore, the enzymatic degradation of PTMC-Ns was accelerated by the surfactants role of lipase via surface erosion mechanism, the enzymatic degradation rate was higher than that of hydrolysis case. The results indicated that PTMC-Ns were promising candidates for clinical subcutaneous implants, especially due to their tunable degradation rate and enhanced form-stability as well as no acidic degradation products.