Surface Topography, Gloss and Flexural Strength of Pressable Ceramic After Finishing-Polishing Protocols
Fernanda P Silva1,2, Ana L R Vilela1, Matheus M G Almeida1
1Department of Operative Dentistry and Dental Materials, School of Dentistry, UFU - Universidade Federal de Uberlândia, Uberlândia, MG, Brazil.
Abstract:
This study evaluated the effect of different finishing-polishing protocols on surface roughness, gloss, morphology and biaxial flexural strength of pressable fluorapatite glass ceramic. Thirty ceramic discs (12x1 mm) were produced and divided into five groups (n=6): CT: control (glaze); DA: fine grit diamond bur; DG: DA + new glaze layer; DP: DA + felt disk with fine grit diamond paste; DK: DA+ sequential polishing with silicon abrasive instruments, goat hair brush and cotton wheel. The specimens were analyzed for surface roughness (Ra) under profilometry and atomic force microscopy (AFM). Gloss was measured with spectrophotometry and micromorphology with scanning electron microscopy (SEM). Flexural strength was assessed by biaxial flexural strength test. Data were analyzed using one-way ANOVA and Tukey's post hoc test (a=0.05). DK showed the lowest surface roughness values and DA presented the highest in the perfilometer analysis. No significant differences were observed in the AFM for the CT, DG and DK groups, which presented the lower surface roughness; DA and DP had the higher Ra values. The DA, DP and CT showed the lowest surface gloss values, and the reflectance was significantly different from those observed for DK and DG groups. SEM analysis revealed the smoothest surface for DK group, followed by DG and CT groups; DA and DP groups exhibited variable degrees of surface irregularities. No significant differences were observed among groups for the biaxial flexural strength. The polishing protocol used in DK group can be a good alternative for chairside finishing of adjusted pressable fluorapatite glass ceramic surfaces.
More Related Videos
06:53Additive Manufacturing of Functionally Graded Ceramic Materials by Stereolithography
Published on: January 25, 2019
08:29Multi-material Ceramic-Based Components – Additive Manufacturing of Black-and-white Zirconia Components by Thermoplastic 3D-Printing (CerAM - T3DP)
Published on: January 7, 2019
Related Concept Videos
01:18Finishing Concrete
01:25Methods of Obtaining Topography
01:16Flexural Stress
Hooke's Law states that within the material's elastic limits, stress is directly proportional to strain. In a member experiencing a bending moment, the strain at any point is relative to its distance...
03:05Acid Strength and Molecular Structure
In the absence of any leveling effect, the acid strength of binary compounds of hydrogen with nonmetals (A) increases as the H-A bond strength decreases down a group in the periodic table. For group 17, the order of increasing acidity is HF < HCl < HBr < HI. Likewise, for group 16, the order of increasing acid strength is H2O < H2S < H2Se < H2Te. Across a row in the periodic table, the acid strength of binary hydrogen compounds increases with increasing...
02:18The Equilibrium Binding Constant and Binding Strength
01:20Strength of Cement
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in...