Fabrication of Highly Crosslinked Gelatin Hydrogel and Its Influence on Chondrocyte Proliferation and Phenotype

Gelatin methacrylate (GelMA) hydrogels have been widely studied for biomedical applications, such as tissue engineering and drug delivery, because of their good biocompatibility and injectability. However, the quick degradation and low mechanical property of GelMA hydrogels need to be improved for further applications, especially for long-term implantation. In this study, a sequential double modification of gelatin was used to achieve high density of photocrosslinkable double bonds in gelatin derivatives. The amino groups in gelatin were first reacted with methacrylic anhydride. After this, the hydroxyl and carboxyl groups in gelatin were reacted with glycidyl methacrylate to obtain the double modified gelatin macromer. The double modified gelatin macromer was used to prepare gelatin hydrogels with high crosslinking density. The hydrogels exhibited high storage modulus and low degradation. Culture of bovine articular chondrocytes in the gelatin hydrogels showed that chondrocytes had round morphology and maintained a cartilaginous phenotype while cell proliferation was hampered. This method for increasing crosslinking density should be useful for preparation of stable hydrogels for cartilage tissue engineering.