Layer-Stacking, Defects, and Robust Superconductivity on the Mo-Terminated Surface of Ultrathin Mo₂C Flakes Grown by...

Materials can exhibit exotic properties when they approach the two-dimensional (2D) limit. Because of promising applications in catalysis and energy storage, 2D transition-metal carbides (TMCs) have attracted considerable attention in recent years. Among these TMCs, ultrathin crystalline α-Mo₂C flakes have been fabricated by chemical vapor deposition on Cu/Mo bilayer foils, and their 2D superconducting property was revealed by transport measurements. Herein, we studied the ultrathin α-Mo₂C flakes by atomic-resolved scanning tunneling microscopy/spectroscopy (STM/S). Strain-related structural modulation and the coexistence of different layer-stacking modes are observed on the Mo-terminated surface of α-Mo₂C flakes as well as various lattice defects. Furthermore, an enhanced superconductivity with shorter correlation length was observed by STS technique, and such superconductivity is very robust despite the appearance of the defects. A mechanism of superconducting enhancement is proposed based on the strain-induced strong coupling and the increased disordering originated from lattice defects. Our results provide a comprehensive understanding of the correlations between atomic structure, defects, and enhanced superconductivity of this emerging 2D material.