Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material
Published on: December 20, 2024
[Effect of intrapulpal pressure on the bonding strength of resin cement to dentin]
1Department of Cariology and Endodontology, Peking University School and Hospital of Stomatology & National Clinical Research Center for Oral Diseases & National Engineering Laboratory for Digital and Material Technology of Stomatology & Beijing Key Laboratory of Digital Stomatology, Beijing 100081, China.
Objective:
To evaluate the effect of intrapulpal pressure simulation on the micro-tensile bond strength (μTBS) of resin cement to dentin.
Methods:
Thirty extracted human third molars were selected. Occlusal enamel was removed to expose dentine surface and teeth with residual dentin thickness of 0.5-2.5 mm were selected. Dye permeation through dentin tubules with or without intrapulpal pressure (IPP) simulation, or after Single Bond Universal (SBU) application on dentin surface with IPP simulation were observed at the end of 0 min, 5 min, 30 min and 2 h. The teeth with residual dentin thickness of (1.0±0.1) mm were divided into 2 groups with IPP simulation of 15 or 0 cmH2O (1 cmH2O=0.098 kPa), which was maintained for 30 min before bonding procedure. SBU was applied on the dentin surface and light cured, then RelyX Ultimate (RLX) cement was heaped on the dentin surface (diameter=10 mm, height=4 mm) and light-cured. After the dentin-resin cement samples were stored in distilled water for 24 h at 37 °C, the samples were cut into beams with cross sectional area of 0.9 mm×0.9 mm for μTSB testing (n=100). The data were analyzed with two independent samples t-test (α=0.05). The fracture mode was observed using scanning electron microscopy (SEM). The results were analyzed with Fisher exact test (α=0.05). The rest of dentin-resin cement samples (five samples for each group) were cut perpendicular to the bonding interface and the morphology of the bonding interface was observed using SEM.
Results:
The dye permeation through dentin tubules with IPP simulation was faster than those without IPP simulation. The μTSB of RLX to dentin with and without IPP simulation were (26.26±9.78) MPa and (28.70±9.0) MPa, respectively. The most frequent fracture mode was mixed-fracture mode. There was no significant difference between the two groups for neither bond strength nor fracture types distribution (P>0.05). Regarding the morphology of dentin-resin cement bonding interface, both groups showed 4-8 μm finger-like resin tags.
Conclusion:
With SBU pretreatment, the IPP simulation had no influence on the immediate bond strength of RLX to dentin.
More Related Videos
07:07Development of a Direct Pulp-capping Model for the Evaluation of Pulpal Wound Healing and Reparative Dentin Formation in Mice
Published on: January 12, 2017
07:33Biological Sample Preparation by High-pressure Freezing, Microwave-assisted Contrast Enhancement, and Minimal Resin Embedding for Volume Imaging
Published on: March 19, 2019
Related Concept Videos
01:20Strength of Cement
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in...
01:12Bonding and Strength of Aggregate
02:49Bond Energies and Bond Lengths
00:42Ionic Bonds
When atoms gain or lose electrons to achieve a more stable electron configuration they form ions. Ionic bonds are electrostatic attractions between ions with opposite charges. Ionic compounds are rigid and brittle when solid and may dissociate into their constituent ions in water. Covalent compounds, by contrast, remain intact unless a chemical reaction breaks them.
Opposing Charges Hold Ions Together in Ionic Compounds
Ionic bonds are reversible electrostatic interactions between ions...
03:05Acid Strength and Molecular Structure
In the absence of any leveling effect, the acid strength of binary compounds of hydrogen with nonmetals (A) increases as the H-A bond strength decreases down a group in the periodic table. For group 17, the order of increasing acidity is HF < HCl < HBr < HI. Likewise, for group 16, the order of increasing acid strength is H2O < H2S < H2Se < H2Te. Across a row in the periodic table, the acid strength of binary hydrogen compounds increases with increasing...
02:43Peptide Bonds