Does airborne-particle abrasion before, rather than after, zirconia sintering lead to higher mechanical strength even
Samira Branco Martins1, Flávia Zardo Trindade2, Márcio de Sousa Góes3
1Doctoral student, Department of Dental Materials and Prosthodontics, Araraquara Dental School, São Paulo State University (UNESP), Araraquara, Brazil.
Statement Of Problem:
Information concerning the effect of airborne-particle abrasion before zirconia sintering on its strength after aging is lacking.
Purpose:
The purpose of this in vitro study was to determine the influence of airborne-particle abrasion moment (before or after zirconia sintering), particle size, and aging on the mechanical strength of a yttria-stabilized tetragonal zirconia polycrystalline (Y-TZP) ceramic.
Material And Methods:
Four hundred presintered zirconia disks were allocated to nonabraded (control) and abraded groups with 50 μm or 120 μm Al2O3 particles before (50/BS or 120/BS) or after sintering (50/AS or 120/AS). The disks were aged by storing them in distilled water for 24 hours at 37 °C (24 h) (control); mechanical cycling (MC) (1×106 cycles; 2 Hz; 100 N); hydrothermal aging (HA) (134 °C; 0.2 MPa; 20 hours); or by both methods (MC+HA), totaling 20 groups (n=20). The specimens were subjected to biaxial flexural strength (BFS) testing. Fractographic analysis was performed to identify the fracture origin. Tetragonal to monoclinic transformation was determined by X-ray diffraction. The BFS data (MPa) were analyzed by 2-way ANOVA and the Games-Howell post hoc test (α=.05). Weibull statistics was also applied.
Results:
The BFS and characteristic strength (σ0) of the 120/AS groups were significantly higher compared with the other abraded groups and statistically similar or higher compared with the respective nonabraded groups. In contrast, the 120/BS/24 h and all the 50/BS groups presented the lowest values. In all groups, the initial defect had its origin on the tensile stress side. Neither airborne-particle abrasion nor aging (except for the 50/AS/MC+HA) reduced the zirconia reliability compared with the respective controls. Abrading the zirconia in its presintered stage or after sintering increased the monoclinic phase content, and the sintering process eliminated this phase.
Conclusions:
Airborne-particle abrasion before zirconia sintering yields an inferior performance compared with that after sintering under aging challenges. The BFS and σ0 were strongly determined by the particle size and airborne-particle abrasion moment, while aging mainly acted in the nonabraded zirconia or when this material was abraded before sintering.
Related Concept Videos
01:23Abrasion Resistance of Concrete
One such test is the revolving disc test, where three plates...
03:05Acid Strength and Molecular Structure
In the absence of any leveling effect, the acid strength of binary compounds of hydrogen with nonmetals (A) increases as the H-A bond strength decreases down a group in the periodic table. For group 17, the order of increasing acidity is HF < HCl < HBr < HI. Likewise, for group 16, the order of increasing acid strength is H2O < H2S < H2Se < H2Te. Across a row in the periodic table, the acid strength of binary hydrogen compounds increases with increasing...
01:20Strength of Cement
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in...
01:30Relation Between Tensile Strength and Compressive Strength of Concrete
02:18The Equilibrium Binding Constant and Binding Strength
03:37Subatomic Particles