Tailoring the synthesis of tantalum-based thin films for biomedical application: Characterization and biological...

The aim of this study was to tailor the deposition parameters of magnetron sputtering to synthetize tantalum oxide (Ta_xO_y) films onto commercially pure titanium (cpTi) surface. The structural and optical properties, morphology, roughness, elemental chemical composition and surface energy were assessed. The impact of Ta_xO_y films on initial Streptococcus sanguinis adhesion was investigated. The morphology and spreading of pre-osteoblastic (MC3T3-E1) cells on a crystalline tantalum oxide film were evaluated. Ta_xO_y films with estimated thickness of 600 nm and different structures (amorphous or crystalline) were produced depending on the various oxygen flow rates and parameters used. X-ray diffraction analysis revealed that the 8 O₂ sccm (600 °C/400 W) group showed crystallization corresponding to the β-Ta₂O₅ phase. Optical analysis showed that the 4 O₂ sccm (200 °C 300 W) to 8 O₂ sccm (600 °C 300 W) groups and 10 O₂ sccm (200 °C 300 W) group presented regular and large-amplitude interference oscillations, suggesting high optical homogeneity of the films. The crystalline β-Ta₂O₅ coating showed higher roughness and surface energy values than the other groups (P < .05) and was biocompatible. Compared with cpTi, the amorphous and crystalline tantalum oxide films did not increase bacterial adhesion (P > .05). By tailoring the deposition parameters, we synthetized a crystalline β-Ta₂O₅ coating that improved titanium surface properties and positively affected cell spreading and morphology, making it a promising surface treatment for titanium-based implants.