Surface morphologic evaluation of orthodontic bonding systems under conditions of cariogenic challenge

Orthodontic bonding systems are submitted to demineralization and remineralization dynamics that might compromise their surface smoothness, and favor biofilm aggregation and caries development. The aim of the present study was to evaluate the effects of a cariogenic challenge model (in vitro pH-cycling model) on the surface roughness and topography of 3 bonding materials: Transbond™ XT (XT), Transbond™ Plus Color Change (PLUS) and Fuji Ortho™ LC (FUJI), by means of Atomic Force Microscopy (AFM). Six specimens with standardized dimensions and surface smoothness were fabricated per group, and the materials were manipulated in accordance with the manufacturers' instructions. No polishing was necessary. AFM tests were performed before and after pH-cycling, taking 3 readouts per specimen. The roughness results (Ra) were obtained at nanometric levels (nm) and surface records were acquired in two- and three-dimensional images of height and lock-in phase of the material components. The surfaces of all groups analyzed in the study were morphologically altered, presenting images suggestive of matrix degradation and loss of matrix-load integrity. FUJI presented the greatest increase in surface roughness, followed by XT and PLUS, respectively (p≤0.001). Nevertheless, the roughness values found did not present sufficient degradation to harbor bacteria. The surface roughness of all tested materials was increased by pH-cycling. The use of materials capable of resisting degradation in the oral environment is recommended, in order to conserve their integrity and of the surrounding tissues.