Synthesis and succinylation of starch nanoparticles by means of a single step using sonochemical energy

In the present research work, esterified nanoparticles with 2-octen-1-ylsuccinic anhydride were synthesized from waxy corn starch, to our knowledge for the first time, in a single step of ultrasonic treatment. First, the ultrasound time to produce non-esterified nanoparticles was studied. The results showed that non-esterified nanoparticles had sizes ranging from 63 to 48 nm, as well as polydispersity indexes (PDI) ranging from 0.458 to 0.224 and ζ-potential values ranging from -16 to -24 mV in ultrasonication times ranging from 20 to 100 min. Succinylated nanoparticles were obtained at 80 min with two degrees of substitution i.e., 0.003 and 0.01, hydrodynamic sizes of 57 and 83 nm, PDI of 0.479 and 0.91, and ζ-potential values of -6.27 and -14.03 mV, respectively. The succinylation of nanoparticles was confirmed by FTIR spectroscopy, and it was possible to elucidate the conversion of amylopectin molecules into amylose blocks. The nanoparticles showed stability during storage in aqueous suspension at 4 °C. By means of the ultrasonic technology, destructuring of the waxy corn starch and, at the same time, the succinylation of the nanoparticles in a total time of 120 min was effectively achieved.