Fracture Resistance and Failure Pattern of Endodontically Treated Teeth Restored with Computer-aided Design/
Rita Eid1, Jelena Juloski2, Hani Ounsi3
1Department of Prosthodontics, Faculty of Dental Medicine, Lebanese University, Beirut, Lebanon, Mobile: 09613695576,
Aim:
To evaluate the fracture resistance and failure pattern of custom made computer-aided design & computer-aided manufacturing (CAD/CAM) post and cores using a fiber reinforced composite material (FRC) and a high-density-polymer.
Materials And Methods:
Thirty extracted mandibular second premolars were selected, endodontically treated and prepared to receive the posts. The specimens were randomly divided into three groups (n = 10) according to each material: group 1 (RXP) : fiber posts (Rely X, 3M-ESPE) with composite core build-up (Filtek Bulk Fill Posterior, 3M-ESPE) as a control group; group 2 (BLC): one-piece milled post and core from fiber reinforced composite blocks (Trilor, Bioloren); and group 3 (AMC): one-piece milled post and core from hybrid ceramic disks (Ambarino, Creamed). All the posts were cemented using a self-adhesive resin cement (Rely X U200, 3M ESPE). Fracture resistance was tested using a universal testing machine, failure patterns were then observed visually and radiographically then evaluated under SEM. Data was analyzed using One-way analysis of variance (ANOVA) followed by Tamhane post-hoc test in order to determine significant differences among groups (α = 0.05).
Results:
The mean fracture resistance values were: 426.08 ± 128.26 N for group 1 (R X P), 367.06 ± 72.34N for group 2 (BLC), and 620.02 ± 54.29N for group 3 (AMC). Statistical analysis revealed that group 3 (AMC) had the highest mean load to fracture in comparison to the other groups (p = 0.000). failures were cohesive in group 2 and 3 and mixed in group 1 with no catastrophic failures reported in all groups.
Conclusion:
All systems evaluated presented sufficient mean load-to-failure values for endodontically treated teeth restorations. CAD/CAM post and cores made from high-density-polymer showed a better performance than prefabricated fiber posts.
More Related Videos
07:42Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material
Published on: December 20, 2024
05:42Detection and Removal of Tooth-Colored Composite Resin Using the Fluorescence-Aided Identification Technique
Published on: July 27, 2022
Related Concept Videos
01:14Design Example: Resistive Touchscreen
When a user touches the screen, the two layers make contact at a specific point known as the touchpoint. This contact reduces the resistance between...
01:15Teeth
In the bud stage, the tooth germ (an aggregation of cells) starts to form in the developing jawbone. During the cap stage, the tooth germ differentiates into enamel organ, dental papilla, and dental sac, which will later develop into the tooth's enamel, dentin...
01:19Restorative Care
02:10The Nucleosome Core Particle
The paradox
Nucleosomes, paradoxically, perform two opposite functions simultaneously. On the one hand, their main responsibility is to protect the delicate DNA strands from physical damage and help achieve a higher compaction ratio. While on the other hand, they must allow polymerase enzymes to access DNA...
01:21Pilot and Numeric Relaying
01:20Study Designs in Epidemiology
Observational studies are those where the researcher does not intervene but rather observes natural variations. They include cross-sectional, cohort, and...