Effect of Er:YAG laser etching on topography, microstructure, compressive strength, and bond strength of a universal
Fereshteh Shafiei1, Paria Dehghanian2, Mahtab Memarpour3
1Oral and Dental Disease Research Center, Department of Operative Dentistry, School of Dentistry, Shiraz University of Medical Sciences, Shiraz, Iran.
Objective:
To evaluate the effect of Er:YAG etching on topography, microstructure, compressive strength, and shear bond strength (SBS) of All-Bond Universal adhesive to mineral trioxide aggregate-Angelus (AMTA) and Biodentine (BD).
Methods And Materials:
Sixty cylindrical specimens of each cement (AMTA and BD) in five groups were prepared and stored for 72 h. The control groups were non-etched, and four other groups were acid-etched and laser-etched with a pulse energy of 60, 80, or 100 mJ, followed by compressive strength testing. Surface micromorphology and topography were evaluated. Similar groups were bonded using All-Bond Universal with self-etch and etch-and-rinse (acid-etch) approaches, and laser-etch 60, 80, and 100 mJ, and SBS was tested. Data were analyzed using two-way and one-way ANOVA and the Bonferroni post hoc tests (α = 0.05).
Results:
BD had a significantly higher compressive strength and SBS (except for laser-etch 100) compared to AMTA, regardless of the etching method (p < 0.001). Acid etching and laser etching 100 of both cements and laser etching 80 of BD alone produced a significantly lower compressive strength than that for the other groups. Contrary to BD, for AMTA, all the treatments significantly increased SBS compared to that of the self-etch group.
Conclusions:
Etching of AMTA was needed for stronger bonding; laser etching with 60 or 80 mJ without compromising compressive strength was recommended. Etching not only did not improve bonding ability of BD, but it also negatively affected the strength of BD.
Clinical Relevance:
To achieve successful combined calcium silicate cement-resin material restoration, an adequate bond between the materials is mandatory. This might be provided with the ultramild adhesive through laser etching without compromising compressive strength, depending on cement composition and laser energy level used.
Related Concept Videos
01:20Strength of Cement
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in...
01:30Relation Between Tensile Strength and Compressive Strength of Concrete
01:12Bonding and Strength of Aggregate
03:05Acid Strength and Molecular Structure
In the absence of any leveling effect, the acid strength of binary compounds of hydrogen with nonmetals (A) increases as the H-A bond strength decreases down a group in the periodic table. For group 17, the order of increasing acidity is HF < HCl < HBr < HI. Likewise, for group 16, the order of increasing acid strength is H2O < H2S < H2Se < H2Te. Across a row in the periodic table, the acid strength of binary hydrogen compounds increases with increasing...
02:18The Equilibrium Binding Constant and Binding Strength
01:29Strength and Heat of Hydration
The heat of hydration for each cement compound is significant; for instance, tricalcium aluminate (C3A) and...