Preparation of high surface area sludge-based activated hydrochar via hydrothermal carbonization and application in
Reza Khoshbouy1, Fumitake Takahashi1, Kunio Yoshikawa1
1Department of Transdisciplinary of Science and Engineering, School of Environment and Society, Tokyo Institute of Technology, Japan.
Abstract:
Conventional methods to produce sludge activated carbon require high-energy due to high moisture content and poor dewaterability of the wet sludge. Recently hydrothermal carbonization (HTC) has been emerged as a promising thermo-chemical wet biowaste conversion technology for the valorization by converting these precursors into high value-added products such as a nanostructured carbon. In this study, sludge-based activated hydrochars (SAC) were prepared from high moisture content (88.9%) wastewater sludge (without pre drying) via HTC followed by physical (P-SAC) and chemical (C-SAC) activation with CO2 and KOH, respectively. Further, the effects of HTC temperatures (170, 200, 230 and 260 °C) and the activation methods on the physicochemical characteristics of hydrochar and SACs were investigated through ultimate analysis (CHNO), SEM, BET, BJH, FT-IR, Boehm back titration and zeta potential. The result showed that KOH-activation at 700 °C could significantly enhance the surface area of hydrochars (from 6.3 to 1613.9 m2/g) compared with CO2-activation even at 900 °C (261.6 m2/g). The mesopore P-SAC prepared from hydrochar at lower HTC temperature due to the presence of ash content. While, the negatively charged microspores C-SAC (VTotal: 0.88 cm3/g and Vmicro/VTotal: 73.3%) with high SBET was synthesized at higher HTC temperature. Prepared hydrochars were applied for the removal of a basic dye (such as methylene blue, MB) from aqueous solution. Based on Langmuir isotherm model (R2>99.4%), the maximum monolayer MB adsorption capacity of hydrochar, P-SAC and C-SAC were 63.3, 122.4, and 588.2 mg/g, respectively at pH > 8.0. The MB adsorption on C-SACs followed the pseudo-second-order kinetic model and a spontaneous endothermic reaction from 298 to 328 K. The commercial ACs also was compared with our materials and found that produced activated hydrochars showed superior results for MB removal. Therefore, HTC can be the potential carbonization method for wet biomass conversion to valuable carbonaceous material in a cost-effective way.
Related Concept Videos
02:27Energy Basics
01:14The Carbon Cycle
01:12Carbon Skeletons
02:52VSEPR Theory and the Basic Shapes
01:22Basic Operations on Signals
Time Reversal mirrors a continuous-time signal about the vertical axis at t=0. This is achieved by substituting t with −t. For example, if a signal x(t) is considered, the time-reversed signal is x(−t). This operation can be graphically represented, showing the mirrored signal.
01:21Basicity of Aliphatic Amines
To measure the basicity of amines, two conventions are generally used. The first defines Kb as the basicity constant for the deprotonation reaction of water by the amine, as presented in Figure 1. Conventionally, lower Kb indicates higher...