High relaxation barrier in neodymium furoate-based field-induced SMMs

Two new neodymium molecular magnets of formula {[Nd(α-fur)₃(H₂O)₂]·DMF}_n (1) and {[Nd_0.065La_0.935(α-fur)₃(H₂O)₂]}_n (2), α-fur = C₄H₃OCOO, have been synthesized. In (1) the furoate ligands, in bidentate bridging mode, consolidate zig-zag chains running along the a-direction. Compound (2) is a magnetically diluted complex of a polymeric chain along the b-axis. Heat capacity, dc magnetization and ac susceptibility measurements have been performed from 1.8 K up to room temperature. Ab initio calculations yielded the gyromagnetic factors g_x* = 0.52, g_y* = 1.03, g_z* = 4.41 for (1) and g_x* = 1.35, g_y* = 1.98, g_z* = 3.88 for (2), and predicted energy gaps of Δ/k_B = 125.5 K (1) and Δ/k_B = 58.8 K (2). Heat capacity and magnetometry measurements agree with these predictions, and confirm the non-negligible transversal anisotropy of the Kramers doublet ground state. A weak intrachain antiferromagnetic interaction J'/k_B = -3.15 × 10^-3 K was found for (1). No slow relaxation is observed at H = 0, attributed to the sizable transverse anisotropy component, and/or dipolar or exchange interactions enhancing the quantum tunnelling probability. Under an external applied field as small as 80 Oe, two slow relaxation processes appear: above 3 K the first relaxation mechanism is associated to a combination of Orbach process, with a sizeable activation energy U/k_B = 121 K at 1.2 kOe for (1), Raman and direct processes; the second, slowest relaxation mechanism is associated to a direct process, affected by phonon-bottleneck effect. For complex (2) a smaller U/k_B = 61 K at 1.2 kOe is found, together with larger g*-transversal terms, and the low-frequency process is quenched. The reported complexes represent rare polymeric Nd single-ion magnets exhibiting high activation energies among the scarce Nd(iii) family.