Effect of silver diamine fluoride and potassium iodide on bonding to demineralized dentin

To evaluate the microtensile bond strength (MTBS) of resin composite to demineralized dentin treated with SDF or SDF-KI.

Occlusal enamel of 30 caries-free extracted human molars was removed to expose flat dentin surfaces. Specimens were immersed in demineralizing solution (pH 4.5) for 7 days. A standard smear layer was created using 600-grit silicon carbide paper. Specimens were distributed into three groups (n=10). Control: Dentin rinsed with deionized water; SDF: Dentin treated with 38% SDF; and SDF-KI: Dentin treated with SDF and KI. Specimens were bonded with composite using Scotchbond Universal in etch-and-rinse mode. MTBS beams were prepared from each specimen after 24 hours and tested. Data was analyzed by one-way ANOVA with Tukey HSD post-hoc test.

MTBS test results ranged from 0 to 40 MPa. The highest values were obtained in the Control and lowest in SDF-KI, where pre-test failures were frequently observed. One-way ANOVA showed a significant difference among groups (P< 0.005); post-hoc analysis suggested no statistical difference between Control and SDF, but both groups showed higher MTBS compared with SDF-KI.

Silver diamine fluoride can be applied precisely and regionally on demineralized dentin before bonding without compromising the bond strength of a universal adhesive used with phosphoric acid etching. Addition of potassium iodide to reduce discoloration will dramatically weaken the bond.