Bioactive glass (45S5)-based 3D scaffolds coated with magnesium and zinc-loaded hydroxyapatite nanoparticles for...

Bioactive glass (BG)-based scaffolds of 45S5 composition covered with hydroxyapatite nanoparticles loaded with Mg²⁺, Zn²⁺ and, both Mg²⁺ and Zn²⁺ ions, were developed and tested as materials for tissue engineering applications. The scaffolds were prepared by the foam replica technique and mono- and bi-metal loaded and unloaded hydroxyapatite nanoparticles (HA, Zn-HA, Mg-HA and Mg-Zn-HA) were obtained by an adaptation of the wet chemical deposition method. Coating of BG with these nanoparticles was performed by dip-coating to obtain HA-BG, Zn-HA-BG, Mg-HA-BG and Mg-Zn-HA-BG scaffolds. As predictor of the bone bonding ability of the produced scaffolds, in this study we investigated the formation of an apatite layer on the scaffold surfaces in the presence of simulated body fluid. The cytotoxicity and osteogenic properties of the materials in vitro was evaluated using human osteoblast-like MG-63 cell cultures. The mineralization assay following Kokubo's protocol indicated that bi-metal loaded Mg-Zn-HA-BG scaffolds exhibited higher/faster bioactivity than mono-metal loaded scaffolds while mineralization of HA-BG, Zn-HA-BG and Mg-HA-BG was similar to that of uncoated scaffolds. Moreover, an increase of proliferation of MG-63 cells after 48 h and 7 days was measured by BrdU assays for Mg-Zn-HA-BG scaffolds. In agreement with these results, SEM images confirmed increased interaction between these scaffolds and cells, in comparison to that observed for mono-metal-loaded HA-coated scaffolds. Altogether, the obtained results suggest that nanocrystalline Mg-Zn-HA coatings enhance the biological performance of standard scaffolds of 45S5 BG composition. Thus these novel ion doped HA coated scaffolds are attractive systems for bone tissue engineering.