Fabrication and Characterization of Zein Composite Particles Coated by Caseinate-Pectin Electrostatic Complexes with...

Zein composite particles coated with caseinate-pectin electrostatic complexes (zein-caseinate-pectin particles) were fabricated using an electrostatic deposition and liquid-liquid dispersion method without heating treatment. Compared to zein particles coated only with caseinate, the acidic stability of zein-caseinate-pectin particles was greatly improved, and the particle aggregation was suppressed at pH 3-6, especially at pH values near the isoelectric point of caseinate (pH 4-5). Besides, desirable long-term storage stability and re-dispersibility were observed. Under different zein to curcumin (Cur) feeding ratios (10:1, 20:1, 30:1 and 40:1, w/w), the Cur-loaded zein-caseinate-pectin particles had a spherical shape with an average diameter ranging from 358.37 to 369.20 nm, a narrow size distribution (polydispersity index < 0.2) and a negative surface charge ranging from -18.87 to -19.53 mV. The relatively high encapsulation efficiencies of Cur (81.27% to 94.00%) and desirable re-dispersibility were also achieved. Fluorescence spectroscopy indicated that the encapsulated Cur interacted with carrier materials mainly through hydrophobic interactions. The in-vitro release profile showed a sustained release of Cur from zein-caseinate-pectin particles in acidic aqueous environment (pH 4) up to 24 h, without any burst effect. In addition, the encapsulation retained more ABTS^•+ radical scavenging capacity of Cur during 4 weeks of storage. These results suggest that zein-caseinate-pectin particles may be used as a potential delivery system for lipophilic nutrients in acidic beverages.