The push out bond strength of polydimethylsiloxane endodontic sealers to dentin

The purpose of this experiment was to assess the push out bond strength of Polydimethylsiloxane sealers (GuttaFlow 2 and GuttaFlow Bioseal by Colte'ne/Whaledent, Altstätten, Switzerland). AH Plus (Dentsply, DeTrey, Konstanz, Germany) was used as a reference material for comparison.

Thirty root slices were prepared from the middle third of 10 mandibular premolars. Each slice was 1 ± 0.1 mm thick. Three holes, 0.8 mm wide each, were drilled on the axial side of each root slice. These holes were subjected to standardized irrigations and then dried using paper points. Finally, for each root slice, each hole was filled with exactly one of the following three root canal sealers: AH Plus, GuttaFlow 2 and GuttaFlow Bioseal. After all the holes were filled in that way, the root slices were stored on top of phosphate-buffered saline solution (pH 7.2) soaked gauze for 7 days at the temperature of 37 degrees Celsius. Then, for each root canal sealer on a root slice, the universal testing machine was used to measure the push out bond strength. The differences in push out bond strengths between the three sealer samples were assessed using the Friedman test, while the paired comparisons were assessed using Wilcoxon signed rank test with Bonferroni correction. All statistical tests were two-tailed and the significance level was set at the 5%.

According to the Friedman test the distributions of push out bond strengths of AH Plus, GuttaFlow 2 and GuttaFlow Bioseal were different (P < 0.05). Paired comparisons indicated that AH Plus had a significantly superior push out bond strength than GuttaFlow 2 and GuttaFlow Bioseal, while the push out bond strength of GuttaFlow Bioseal was significantly stronger than that of GuttaFlow 2 (P < 0.01).

Based on these findings, AH Plus is a better root canal sealer than GuttaFlow 2 and GuttaFlow Bioseal.