A promising form-stable phase change material prepared using cost effective pinecone biochar as the matrix of...

A promising new form-stable phase change material (PA/PB) was fabricated using pinecone biochar (PB) as the supporting material of palmitic acid (PA). The biochar of PB with large surface area was produced by forest residue of pinecone, and it was cheap, environment friendly and easy to prepare. The PB was firstly utilized as the supporter of PA and the characterizations of PA/PB were analyzed by the BET, SEM, XRD, DSC, TGA, FT-IR and thermal conductivity tester. The results demonstrated that the PA was physically absorbed by the PB and the crystal structure of the PA was not destroyed. The results of DSC showed that the fusing and crystallization points of the form-stable phase change material with the maximum content of PA (PA/PB-4) were 59.25 °C and 59.13 °C, and its fusing and freezing latent heat were 84.74 kJ/kg and 83.81 kJ/kg, respectively. The results of TGA suggested that the thermal stability of the PA/PB-4 composite was excellent, which could be used for the applications of thermal energy storage. Furthermore, the thermal conductivity of PA/PB-4 was 0.3926 W/(m∙K), which was increased by 43.76% compared with that of the pure PA. Thus, the study results indicated that the PA/PB-4 had great potential for thermal energy storage applications.