Effect of cooling protocol on mechanical properties and microstructure of dental veneering ceramics
Carina B Tanaka1, Nur Hanani Binti Ahmad1, Ayman Ellakwa2
1School of Mechanical and Manufacturing Engineering, UNSW Sydney, Sydney NSW 2052, Australia.
Objectives:
Understand how cooling protocols control the microstructure and mechanical properties of veneering porcelains.
Methods:
Two porcelain powders were selected, one used to veneer metallic frameworks (VM13) and one for zirconia frameworks (VM9). After the last firing cycle, the monolithic specimens were subjected to two cooling protocols: slow and fast. Flexural strength (FS) was evaluated by three-point beam bending and fracture toughness (KIC) was evaluated by the single-edge V-notch beam (SEVNB) method. Scanning electron microscopy (SEM) was performed to determine the leucite crystal volume fraction (%), particle size, and matrix microcrack density. The results were compared by analysis of variances (ANOVA) and Tukey's multiple comparison test.
Results:
The mechanical properties were significantly (p<0.05) higher for the VM13 porcelain (FS=111.0MPa, KIC=1.01MPa.√m) compared to VM9 (FS=79.6MPa, KIC =0.87MPa.√m) regardless of cooling protocol due to ∼250% higher volume fraction of leucite crystals. The slow cooled VM13 and fast cooled VM9 resulted in the highest and lowest mechanical properties, respectively, while the VM9 slow cooled properties were similar to the VM13 fast cooled. The SEM revealed that the slow cooling significantly increased the volume fraction of leucite crystals by 33-41 %. Across both porcelains, a significant linear correlation between both mechanical properties (strength and toughness) and leucite crystal content was found. Slow cooling was also associated with increased crystal growth resulting in more matrix microcracking.
Significance:
Controlled crystallization using slow cooling can be applied as a means of strengthening dental porcelains. However, the benefits of slow cooling may be partially offset by increasing the microcrack density in the glass matrix. To achieve the maximum benefit of slow cooling, it is recommending to develop heat treatments to produce porcelain with fine-grained and homogenously dispersed leucite crystals to achieve minimal glass matrix microcracking.
More Related Videos
Related Concept Videos
01:19Veneer
Other veneering techniques include plain-slicing, quarter-slicing, and rift-slicing. These...
02:44Heating and Cooling Curves
For instance, the addition of heat raises the temperature of a solid; the amount of heat absorbed depends on the heat capacity of the solid (q = mcsolidΔT). According to thermochemistry, the relation between the amount of heat absorbed or released by a substance, q, and its...
02:57Physical and Chemical Properties of Matter
02:58Properties of Transition Metals
02:19Physical Properties Affecting Solubility
As for any solution, the solubility of a gas in a liquid is affected by the attractive intermolecular forces between solute and solvent species. Unlike solid and liquid solutes, however, there is no solute-solute intermolecular attraction to overcome when a gaseous solute dissolves in a liquid solvent since the atoms or molecules comprising a gas are far separated and experience negligible interactions. Consequently, solute-solvent interactions are the sole...
02:45The Quantum-Mechanical Model of an Atom