Enhanced Cyclability and High-Rate Capability of LiNi_0.88Co_0.095Mn_0.025O₂ Cathodes by Homogeneous Al³⁺ Doping

To suppress capacity fading of nickel-rich materials for lithium-ion batteries, a homogeneous Al³⁺ doping strategy is realized through tailoring the Al³⁺ diffusion path from the bulk surface to interior. Specifically, the layered LiNi_0.88Co_0.095Mn_0.025O₂ cathode with the radial arrangement of primary grains is successfully synthesized through optimization design of precursors. The Al³⁺ follows the radially oriented primary grains into the bulk by introduction of nano-Al₂O₃ during the sintering process, realizing the homogeneous Al³⁺ distribution in the whole material. Particularly, a series of nano-Al₂O₃-modified LiNi_0.88Co_0.095Mn_0.025O₂ are investigated. With the 2% molar weight of Al³⁺ doping, the capacity retention ratio of the cathode is tremendously improved from 52.26 to 91.57% at 1 C rate after 150 cycles. Even at a heavy current density of 5 (&10) C for the LiNi_0.88Co_0.095Mn_0.025O₂-Al_2% cathode, a high reversible capacity of 172.3 (&165.7) mA h g^-1 can be acquired, which amount to the 84.46 (&81.25) % capacity retention at 0.2 C. Moreover, voltage deterioration is significantly suppressed by homogeneous Al³⁺ doping from the results of median voltage and dQ/dV curves. Therefore, homogeneous Al³⁺ doping benefited from the radial arrangement of primary grains provides an effective and practical way to prolong lifespan, as well as improves rate performance and voltage stability of nickel-rich ternary materials.