Lanthanum Hydroxide Nanorod-Templated Graphitic Hollow Carbon Nanorods for Supercapacitors

Lanthanum hydroxide nanorods were employed as both a template and catalyst for carbon synthesis by chemical vapor deposition. The resulting carbon possesses hollow nanorod shapes with graphitic walls. The hollow carbon nanorods were interconnected at some junctions forming a mazelike network, and the broken ends of the tubular carbon provide accessibility to the inner surface of the carbon, resulting in a surface area of 771 m²/g. The hollow carbon was tested as an electrode material for supercapacitors. A specific capacitance of 128 F/g, an energy density of 55 Wh/kg, and a power density of 1700 W/kg at 1 A/g were obtained using the ionic liquid, 1-ethyl-3-methylimidazolium bis(trifluoromethylsulfonyl)imide, as the electrolyte.