Green Synthesis of Novel Polyesterurethane Materials from Epoxides and Carbon Dioxide by New Set of One-Dimensional...

Two novel polyesterurethane materials, PEU1 and PEU2, were synthesized via nontoxic and isocyanate-free route by simple conversion of two epoxides 1,2-epoxy-3-phenoxy propane (2) and styrene epoxide (3) utilizing CO₂. Epoxides 2 and 3 were converted to the respective cyclic carbonates 4 and 5 by a new set of cobalt-based catalyst 1a in the presence of 10 bar of CO₂ and 80 °C temperature without using cocatalyst tetrabutylammonium bromide (TBAB). The mechanistic pathway of the catalysis reaction for the cycloaddition of epoxides with CO₂ to generate the cyclic carbonates was investigated by several spectroscopic techniques and utilizing analogous zinc-based 1D coordination polymer 1b, which does not act as an efficient catalyst in the absence of TBAB. Cyclic carbonates 4 and 5 were converted to the respective polyesterurethanes PEU1 and PEU2 sequentially by first synthesizing the ring-opened diols 6 and 7 reacting with ethylenediamine and subsequently annealing the respective diols 6 and 7 at 120 °C in the presence of terepthalyl chloride and triethylamine. The polyesterurethanes PEU1 and PEU2 were characterized by multinuclear NMR and FTIR. PEU1 was also characterized by MALDI-TOF mass spectrometry. The thermal studies of PEU1 and PEU2 showed the stability up to 200-270 °C. The number-average and weight-average molecular weights were determined for PEU1 and PEU2 by GPC analysis. The weight-average molecular weight for PEU1 was found to be 5948 with a polydispersity of 1.1, and PEU2 showed the weight-average molecular weight as 4224 with a polydispersity of 1.06.