The Self-Passivation Mechanism in Degradation of BiVO₄ Photoanode

BiVO₄ is a promising photoanode material for solar-assisted water splitting in a photoelectrochemical cell but has a propensity to degrade. Investigations carried out here in 0.1 M Na₂SO₄ electrolyte showed that degradation is by dissolution of V in the electrolyte while Bi is retained on the anode probably in the form of solid Bi oxide (Bi₂O₃, Bi₄O₇). Accumulation of Bi oxide on the anode surface leads to passivation from further degradation. Thermodynamic modeling of possible degradation reactions has provided theoretical support to this mechanism. This self-passivation is accompanied by a decrease in photocurrent density, but it protects the anode against extensive photocorrosion and contributes to long-term stability. This is a more definitive understanding of degradation of BiVO₄ during water splitting in a photoelectrochemical cell. This understanding is imperative for both fundamental and applied research.