A Bilayer 2D-WS₂/Organic-Based Heterojunction for High-Performance Photodetectors

Two-dimensional (2D) tungsten disulfide (WS₂) has inspired great efforts in optoelectronics, such as in solar cells, light-emitting diodes, and photodetectors. However, chemical vapor deposition (CVD) grown 2D WS₂ domains with the coexistence of a discontinuous single layer and multilayers are still not suitable for the fabrication of photodetectors on a large scale. An emerging field in the integration of organic materials with 2D materials offers the advantages of molecular diversity and flexibility to provide an exciting aspect on high-performance device applications. Herein, we fabricated a photodetector based on a 2D-WS₂/organic semiconductor materials (mixture of the (Poly-(N, N'-bis-4-butylphenyl-N, N'-bisphenyl) benzidine and Phenyl-C61-butyric acid methyl ester (Poly-TPD/PCBM)) heterojunction. The application of Poly-TPD/PCBM organic blend film enhanced light absorption, electrically connected the isolated WS₂ domains, and promoted the separation of electron-hole pairs. The generated exciton could sufficiently diffuse to the interface of the WS₂ and the organic blend layers for efficient charge separation, where Poly-TPD was favorable for hole carrier transport and PCBM for electron transport to their respective electrodes. We show that the photodetector exhibited high responsivity, detectivity, and an on/off ratio of 0.1 A/W, 1.1 × 10¹¹ Jones, and 100, respectively. In addition, the photodetector showed a broad spectral response from 500 nm to 750 nm, with a peak external quantum efficiency (EQE) of 8%. Our work offers a facile solution-coating process combined with a CVD technique to prepare an inorganic/organic heterojunction photodetector with high performance on silicon substrate.