Preparation of Polyethylene and Ethylene/Methacrylic Acid Copolymer Blend Films with Tunable Surface Properties...

Polymer films based on polyethylene (PE) and ionomer ethylene/methacrylic acid (EMAA) copolymer blend were prepared by film blowing, whose surface properties were tuned by varying processing parameters, i.e., take up ratio (TUR). Blends of PE/EMAA copolymer were firstly prepared by the melt-mixing method, before being further blown to films. The wettability of the film was investigated by measuring the contact angle/water-film encounter time, and optical properties, i.e., the haze and transmittance. The wettability was found to be enhanced with the increase of TUR. So too was the haze, while the transmittance was found to be almost independent of TUR. The XPS and AFM results directly show the increasing polar functional groups (-COO^-) on the surface and roughness with increasing TUR. Further analysis of the 2D SAXS and WAXS unveiled the origin of the invariant transmittance, which resulted from the minor change of the crystallinity and the monotonic increase of the haze, with TUR resulting from the evolution of crystal orientation. In addition to other post-modification methods, the current study provides an alternative route to prepare large-scale PE films as the template for the advanced potential applications, i.e., covering in the layer of roof, the privacy of protective windows, and multitudes of packaging.