Preparation of Stable Silver Nanoparticles Having Wide Red-To-Near-Infrared Extinction

The synthesis of silver nanoparticles (AgNPs) within the interlayer space of transparent layered titania nanosheet (TNS) films is investigated. A considerable number of silver ions (≈70% against the cation exchange capacity of the TNS) are intercalated in the TNS films using methyl-viologen-containing TNSs as a precursor. The silver ion (Ag⁺)-containing TNS films are treated with aqueous sodium tetrahydroborate (NaBH₄), resulting in a gradual color change to bright blue. Various structural analyses clearly show that crystalline AgNPs are generated within the interlayer space of the TNSs. The NaBH₄-treated films show intense and characteristic near-infrared (NIR) extinction spectra up to 1800 nm. The stability of the AgNPs within the TNS against oxygen and moisture is also investigated, and 96% and 82% of the AgNPs remain after standing in air for 1 month and 1 year, respectively. The NIR extinctions of the AgNP-containing TNS films are further extended by employing different preparation procedures, for example, using sintered TNS films as starting materials and irradiating the Ag⁺-containing TNSs with ultraviolet (UV) light. The obtained AgNP-containing TNS films exhibit photochemical activities in the production of hydrogen from ammonia borane under visible-light irradiation and the decomposition of nitrogen monoxide under UV-light irradiation.