Macroporous Oil-Sorbents with a High Absorption Capacity and High-Temperature Tolerance Prepared through
Abdul Haleem1, Jia-Yun Wang2, Hui-Juan Li3
1CAS Key Laboratory of Soft Matter Chemistry, Department of Polymer Science and Engineering, University of Science and Technology of China, Hefei, Anhui 230026, China. haleem@mail.ustc.edu.cn.
Abstract:
The facile preparation and admirable performance of macro-porous poly(lauryl acrylate)-based oil-sorbents for organic solvents and oils are reported in this manuscript. Cryo-polymerizations of lauryl acrylate (LA) with ethylene glycol dimethacrylate (EGDMA) as the cross-linker were carried out at temperatures below the freezing point of the polymerization mixture. The polymerization medium and pore-forming agent was 1,4-dioxane. The influences of the total monomer concentration, EGDMA content and cryo-polymerization temperature on the structure of the obtained P(LA-co-EGDMA) cryogels were investigated with the techniques of Fourier transform infrared spectroscopy, scanning electron microscopy, contact angle measurement and thermo-gravimetric analysis. Through the modulation of the crosslinking density and porosity of these cryogels, the P(LA-co-EGDMA) oil-sorbents demonstrated a high absorption capacity for organic solvents and oils, recyclability and high-temperature tolerance. The absorption capacity reached 20-21 and 16-17 g/g for toluene and gasoline oil, respectively. Those fabricated sorbents survived high temperatures up to 150 °C without any change in absorption capacity as well as porosity. Considering the convenient synthesis process and absorption performance, the present work offers a remarkable opportunity to bring polymer cryogels to practical application in waste oil clean-up.