Effect of Multilayering Incremental Technique on the Microleakage of High-viscosity Bulk-fill Composite Restorations
Mohammed K Fahmi1, Amal A Ashour2, Vipin Arora3
1Department of Restorative Dental Sciences, Faculty of Dentistry, Taif University, Taif, Kingdom of Saudi Arabia.
Aim:
The aim of this study is to evaluate the effect of multilayering incremental technique on the microleakage of high-viscosity bulk-fill composite restorations in endodontically treated teeth.
Materials And Methods:
A total of 60 human mandibular premolar teeth were divided into four groups after standardized access preparation with a protaper technique followed by single-cone obturation to receive the following restorations for the access preparations. Group I (n = 20): bulk-fill composite (Filtek™ Bulk fill) using a bulk technique, group II (n = 20): bulk-fill composite (Filtek™ Bulk fill) using an incremental layering technique, group III (negative control) (n = 10): gutta-percha was kept intact at the access orifice and covered with a nail polish, and group IV (positive control) (n = 10): gutta-percha was kept intact at the orifice. The samples were thermocycled at 5°C and 55°C for 500 cycles followed by dye penetration with 2% methylene blue and then the scoring was done under a stereomicroscope at 10× magnification. The data so obtained were compared for microleakage using a Chi-square test. There was a significant difference among all the groups except groups II and III.
Results:
Bulk-fill composites used with an incremental layering technique sealed significantly better than the other groups followed by bulk-fill composite in the bulk technique.
Conclusion:
Within the limitations of the present study, it can be concluded that the incremental layering technique with bulk-fill composites significantly decreases microleakage in the restored access preparations of endodontically treated teeth.