Antibacterial, physical and mechanical properties of bonding agent containing synthesized Zinc Dimethacrylate

The aim of this study includes synthesis of zinc dimethacrylate ionomer (ZDMA) by a new method, incorporate it into resin bonding and evaluate its antibacterial, physical and mechanical properties.

Resin adhesives containing 0 to 5% wt of ZDMA was produced and the following tests were accomplished: A: Antibacterial test: 1.Direct contact test. 2.Material aging; in both of them the bacterial colony counting were performed. B: Physical test: 1.Degree of conversion (D.C). 2.Evaluating the amount of released Zinc ion release in aqueous medium. C: Mechanical test: 1.Compressive strength test. 2.Shear bond test (enamel and dentine separately). The obtained results were statistically analyzed using One Way ANOVA and LSD post hoc test (α=0.05).

The anti-bacterial test revealed that all the ZDMA containing groups significantly reduced the amount of Streptococcus Mutans bacteria. Moreover, the D.C in all ZDMA groups was enhanced. Furthermore, ion release analysis revealed noticeable stability of Zn2+ in samples, as in the 5wt.% group it was even after nine cycle of 24h wash. On the other hand, the compressive strength was significantly reduced just in the 5% ZDMA group while the other groups were superior comparing to the control. In addition, there was no significant difference among the enamel shear bond strength of the groups. However, about the dentine shear bond strength, only the 5% ZDMA group was significantly higher than the control.

Low percentages of ZDMA in adhesive could impart anti-bacterial efficacy without challenging its mechanical and physical properties. Key words:Dental Resin Bonding, Zinc, Streptococcus mutans, Degree of conversion, Compressive strength.