Fabrication and Properties of Superhydrophobic Waterborne Polyurethane Composites with Micro-Rough Surface Structure...

Waterborne polyurethane (WPU) coatings hold advantages of good toughness, low cost and environmental protection. However, the low water contact angle (WCA), poor wear and corrosion resistance make them unsuitable for application in the superhydrophobic coatings such as antipollution flashover coatings for transmission lines, self-cleaning coatings for outdoor equipment and waterproof textiles. A series of superhydrophobic WPU composites (SHWPUCs) with micro-rough surface structure was prepared by electrostatic spraying nano-SiO₂ particles on WPU composites with low surface energy. It showed that as the hydrophobic system content rose the WCAs of the composites first increased and then remained stationary; however, the adhesion and corrosion resistance first increased and then decreased. An appropriate addition of the hydrophobic system content would lead to a dense coating structure, but an excessive addition could increase the interfaces in the coating and then reduce the coating performance. When the mass ratio of the WPU dispersion, polytetrafluoroethylene (PTFE) particles and modified polydimethylsiloxane was 8:0.3:0.4, 10 g/m² nano-SiO₂ particles were sprayed on the uncured coating surface to construct the SHWPUC with a WCA of 156°. Compared with pure WPU coating, its adhesion and corrosion resistance increased by 12.5% and one order of magnitude, respectively; its wear rate decreased by 88.8%.