Measurement of Heat Dissipation and Thermal-Stability of Power Modules on DBC Substrates with Various Ceramics by SiC...

This study introduced the SiC micro-heater chip as a novel thermal evaluation device for next-generation power modules and to evaluate the heat resistant performance of direct bonded copper (DBC) substrate with aluminum nitride (AlN-DBC), aluminum oxide (DBC-Al₂O₃) and silicon nitride (Si₃N₄-DBC) ceramics middle layer. The SiC micro-heater chips were structurally sound bonded on the two types of DBC substrates by Ag sinter paste and Au wire was used to interconnect the SiC and DBC substrate. The SiC micro-heater chip power modules were fixed on a water-cooling plate by a thermal interface material (TIM), a steady-state thermal resistance measurement and a power cycling test were successfully conducted. As a result, the thermal resistance of the SiC micro-heater chip power modules on the DBC-Al₂O₃ substrate at power over 200 W was about twice higher than DBC-Si₃N₄ and also higher than DBC-AlN. In addition, during the power cycle test, DBC-Al₂O₃ was stopped after 1000 cycles due to Pt heater pattern line was partially broken induced by the excessive rise in thermal resistance, but DBC-Si₃N₄ and DBC-AlN specimens were subjected to more than 20,000 cycles and not noticeable physical failure was found in both of the SiC chip and DBC substrates by a x-ray observation. The results indicated that AlN-DBC can be as an optimization substrate for the best heat dissipation/durability in wide band-gap (WBG) power devices. Our results provide an important index for industries demanding higher power and temperature power electronics.