Mass spectrometry and ion mobility study of poly(ethylene glycol)-based polyurethane oligomers

Commercial-grade polymer synthesis is performed via melt polymerization, which leads to polydispersion. The work reported herein provides a synthetic strategy to produce mono-dispersive polyurethane oligomers and an analytical strategy to distinguish these oligomers, providing chemists with the tools necessary to synthesize and identify specific polymer structures that exhibit a desired property.

Three isomeric poly(ethylene glycol)-polyurethane (PEG-PUR) oligomers were synthesized and analyzed via flow-injection ion mobility mass spectrometry (IM-MS). Each polymer oligomer was injected and run independently via flow injection at 100 μL•min^-1 and analyzed in positive ion mode on a drift tube quadrupole time-of-flight (QTOF) instrument. Mobility measurements were determined using a single-field approach. For tandem mass spectrometry (MS/MS) experiments, the sodium-adducted singly charged precursor ion was isolated in the quadrupole and subjected to a range of collision energies.

In MS experiments, both +1 and +2 sodium-adducted species were observed for each oligomer at m/z 837.4 and 430.2, respectively. When isolated and fragmented via MS/MS, the +1 precursor yielded distinct product ions for each of the three isomeric oligomers. Fragmentation generally occurred at urethane linkages via 1,3- and 1,5-H shift mechanisms. IM was also used to distinguish the three isomers, with greater IM separation observed for the +2 versus the +1 species.

Mono-disperse PEG-PUR oligomers were synthesized and analyzed. Although the polymeric oligomers analyzed in this study are quite small and structurally simple, this work serves as a model system for the synthesis and structural characterization of larger, more complex block copolymers.