Ni-Based Catalyst Derived from NiAl Layered Double Hydroxide for Vapor Phase Catalytic Exchange between Hydrogen and
Xiaoyu Hu1,2, Peilong Li2, Xin Zhang2
1School of Resource Environmental and Safety Engineering, University of South China, Hengyang 421001, China.
Abstract:
A high-efficient and low-cost catalyst on hydrogen isotope separation between hydrogen and water is an essential factor in industrial application for heavy water production and water detritiation. In past studies, Pt-based catalysts were developed but not practical for commercial use due to their high cost for vapor phase catalytic exchange (VPCE), while for impregnated nickel catalysts with a lower cost the problems of agglomeration and low Ni utilization existed. Therefore, to solve these problems, in-situ grown Ni-based catalysts (NiAl-LDO) derived from a layered double hydroxide (LDH) precursor were fabricated and first applied in VPCE in this work. Compared with traditional impregnated Ni-based catalysts, NiAl-LDO catalysts own a unique layered structure, homogeneous dispersed metallic phase, higher specific surface area as well as stronger metal-support interactions to prevent active metal from agglomerating. These advantages are beneficial for exposing more active sites to improve dynamic contacts between H2 and HDO in a catalyst surface and can bring excellent catalytic activity under a reaction temperature of lower than 400 °C. Additionally, we found that the dissociative chemisorption of HDO and H2 occurs not only in Ni (111) but also in NiO species where chemisorbed H(ads), D(ads), OH(ads) and OD(ads) are formed. The results highlight that both of the Ni2+ species and Ni0 species possess catalytic activities for VPCE process.
More Related Videos
Related Concept Videos
02:17Reduction of Alkenes: Asymmetric Catalytic Hydrogenation
The metal catalyst used can be either heterogeneous or homogeneous. When hydrogenation of an alkene generates a chiral center, a pair of enantiomeric products is expected to form. However, an enantiomeric excess of one of the products can be facilitated using an enantioselective reaction or an...
02:50Catalysis
02:13Reduction of Alkenes: Catalytic Hydrogenation
Metals like palladium, platinum, and nickel are commonly used in their solid forms — fine powder on an inert surface. As these catalysts remain insoluble in the reaction mixture, they are referred to as heterogeneous catalysts.
The hydrogenation process takes place on the...
02:24Reduction of Alkynes to cis-Alkenes: Catalytic Hydrogenation
Like alkenes, alkynes can be reduced to alkanes in the presence of transition metal catalysts such as Pt, Pd, or Ni. The reaction involves two sequential syn additions of hydrogen via a cis-alkene intermediate.
01:20Aldehydes and Ketones with Water: Hydrate Formation
The formation of hydrates is a reversible reaction. Hydrate formation is influenced by steric and electronic factors accompanying the alkyl substituents on the carbonyl group: The rate of hydrate formation increases with a decrease in the number of alkyl groups attached to the carbonyl carbon. Hence,...
02:23Alcohols from Carbonyl Compounds: Reduction
Catalytic hydrogenation is similar to the reduction of an alkene or alkyne by adding H2 across the pi bond in the presence of transition metal catalysts like Raney Ni, Pd–C, Pt, or Ru. Aldehydes and ketones can be reduced by this method, often under mild to moderate heat (25–100°C) and...