Characterization of ionic cross-linked composite foams with different blend ratios of alginate/pectin on the
Gun-Woo Oh1, Seung Yun Nam1, Soo-Jin Heo2
1Department of Biomedical Engineering, and Center for Marine-Integrated Biomedical Technology (BK21 Plus) Pukyong National University, Busan 48513, Republic of Korea; Marine-Integrated Bionics Research Center, Pukyong National University, Busan 48513, Republic of Korea.
Abstract:
Alginate and pectin have been widely employed together in various industrial and biomedical applications due to their synergistic interaction. Although alginate and pectin have been used as composite materials in films, gels, and particles, research characterizing their properties in foams is scarce. Thus, in the present study, we fabricated alginate-pectin composite foams with different blending ratios (9:1, 7:3, and 5:5) using calcium ion cross-linking and characterized their properties. It was found that the G' values of rehydrated alginate-pectin 9:1 foam was higher than those of the other rehydrated foams in the rheological behavior. In addition, higher pectin levels in the composite foams led to more water being absorbed during swelling tests and the higher release of BSA in drug-release testing. In indirect and direct cytotoxicity testing, none of the foams exhibited cell cytotoxicity for fibroblast and keratinocyte cells. These results suggest that controlling the pectin content in alginate-pectin foams is key to adjusting their mechanical properties, water absorption, and drug-release ability. In addition, alginate-pectin composite foams are promising candidates for use in wound-dressing applications.