Conversion of a Defect Pyrochlore into a Double Perovskite via High-Pressure, High-Temperature Reduction of Te6

Fabio Denis Romero1,2, Midori Amano Patino1, Mitsutaka Haruta1

  • 1Institute for Chemical Research , Kyoto University , Gokasho, Uji , Kyoto 611-0011 , Japan.

Inorganic Chemistry
|December 11, 2019
PubMed

More Related Videos

High Pressure Single Crystal Diffraction at PX^211:32

High Pressure Single Crystal Diffraction at PX^2

Published on: January 16, 2017

22.0K
Flash Infrared Annealing for Perovskite Solar Cell Processing05:15

Flash Infrared Annealing for Perovskite Solar Cell Processing

Published on: February 3, 2021

8.5K

Related Concept Videos

Imperfections in Crystal Structure: Stoichiometric Point Defects01:26

Imperfections in Crystal Structure: Stoichiometric Point Defects

Schottky defects arise when some lattice points in a crystal, such as those in NaCl, remain unoccupied, creating lattice vacancies without disturbing the overall electrical neutrality of the crystal. This defect is common in ionic crystals where the positive and negative ions are similar in size, as seen in sodium chloride and cesium chloride. The presence of Schottky defects enables the crystal to conduct electricity to a small extent through an ionic mechanism. Electric fields cause nearby...
Imperfections in Crystal Structure: Non-Stoichiometric Defects01:29

Imperfections in Crystal Structure: Non-Stoichiometric Defects

Non-stoichiometric defects refer to a type of defect in the crystal structure of a compound where the ratio of its constituent elements deviates from the ideal stoichiometric ratio. There are two main types of non-stoichiometric defects: metal excess defects and metal deficiency defects.Metal excess defects occur when there is a slight surplus of metal ions than what is required by the stoichiometric ratio of the compound. For example, heating a sodium chloride crystal in sodium vapor results...