Kerf Taper Defect Minimization Based on Abrasive Waterjet Machining of Low Thickness Thermoplastic Carbon Fiber...

Carbon fiber-reinforced thermoplastics (CFRTPs) are materials of great interest in industry. Like thermosets composite materials, they have an excellent weight/mechanical properties ratio and a high degree of automation in their manufacture and recyclability. However, these materials present difficulties in their machining due to their nature. Their anisotropy, together with their low glass transition temperature, can produce important defects in their machining. A process able to machine these materials correctly by producing very small thermal defects is abrasive waterjet machining. However, the dispersion of the waterjet produces a reduction in kinetic energy, which decreases its cutting capacity. This results in an inherent defect called a kerf taper. Also, machining these materials with reduced thicknesses can increase this defect due to the formation of a damage zone at the beginning of cut due to the abrasive particles. This paper studies the influence of cutting parameters on the kerf taper generated during waterjet machining of a thin-walled thermoplastic composite material (carbon/polyurethane, C/TPU). This influence was studied by means of an ANOVA statistical analysis, and a mathematical model was obtained by means of a response surface methodology (RSM). Kerf taper defect was evaluated using a new image processing methodology, where the initial and final damage zone was separated from the kerf taper defect. Finally, a combination of a hydraulic pressure of 3400 bar with a feed rate of 100 mm/min and an abrasive mass flow of 170 g/min produces the minimum kerf taper angle.