Efficient Bifacial Passivation with Crosslinked Thioctic Acid for High-Performance Methylammonium Lead Iodide...

Defects, inevitably produced within bulk and at perovskite-transport layer interfaces (PTLIs), are detrimental to power conversion efficiency (PCE) and stability of perovskite solar cells (PSCs). It is demonstrated that a crosslinkable organic small molecule thioctic acid (TA), which can simultaneously be chemically anchored to the surface of TiO₂ and methylammonium lead iodide (MAPbI₃ ) through coordination effects and then in situ crosslinked to form a robust continuous polymer (Poly(TA)) network after thermal treatment, can be introduced into PSCs as a new bifacial passivation agent for greatly passivating the defects. It is also discovered that Poly(TA) can additionally enhance the charge extraction efficiency and the water-resisting and light-resisting abilities of perovskite film. These newly discovered features of Poly(TA) make PSCs herein achieve among the best PCE of 20.4% ever reported for MAPbI₃ with negligible hysteresis, along with much enhanced ultraviolet, air, and operational stabilities. Density functional theory calculations reveal that the passivation of MAPbI₃ bulk and PTLIs by Poly(TA) occurs through the interaction of functional groups (COOH, CS) in Poly(TA) with under-coordinated Pb²⁺ in MAPbI₃ and Ti⁴⁺ in TiO₂ , which is supported by X-ray photoelectron spectroscopy and Fourier transform infrared spectroscopy.