Effect of staining and repeated firing on the surface and optical properties of lithium disilicate
Jean S Miranda1, Aline S P Barcellos1, Carolina M MartinelliLobo1
1Department of Dental Materials and Prosthodontics, São José dos Campos Dental School, Institute of Science and Technology, UNESP-Paulista State University, São José dos Campos, Brazil.
Objective:
Evaluate the effect of staining and repeated firings on color, translucency and surface proprieties of CAD/CAM lithium disilicate (LD).
Material And Methods:
One hundred eighty LD discs were made (ISO 6872) and distributed in different groups (n = 20): control (CO)-no treatment; single-step characterization (SC)-crystallization and staining fired together; and double step characterization (DC)-crystallization and then staining. The samples were submitted to two, four, or six firings, resulting in nine groups: COII, COIV, COVI, SCII, SCIV, SCVI, DCII, DCIV, and DCVI. The color and translucency were measured by a reflectance spectrophotometer. Surface roughness (Ra) and Vickers nano-hardness were also measured. ANOVA and Tukey statistical tests were used (α = .05).
Results:
Only CO and DC demonstrated significant color alterations (ΔE00 > 1.8). SC and DC did not show changes in translucency by the number of firings (P > .05); however, for CO (P = .02) these values increased. Nano-hardness was similar in all groups (P > .05). Ra values indicated differences due to the type of characterization (SC presented the highest values) and number of firings (CO and DC groups) (P < .01).
Conclusion:
SC promoted color, translucency, and roughness stability after repeated firings.
Clinical Significance:
The single characterization technic in CAD/CAM lithium disilicate presents good color, translucency, and hardness stability, which promote predictable results to monolithic restoration.