Controlled Phase Behavior of Thermally Sensitive Poly(N-isopropylacrylamide/ionic liquid) with Embedded Au
Surabhi Gupta1, Ankit Singh1, Noriyoshi Matsumi1
1School of Materials Science, Japan Advanced Institute of Science and Technology, 1-1 Asahidai, Nomi, Ishikawa 923 1292, Japan.
Abstract:
We have synthesized a series of poly(N-isopropylacrylamide/ionic liquid) with deposited Au nanoparticles. The size of the nanoparticle range was varied from 10 to 35 nm, and these were characterized by transmission electron microscopy analysis. Ionic liquids (IL) were chosen by varying the polymerizable unit to be both in cationic (allyl) and anionic (acrylate) moiety. One-pot polymerization was done with N-isopropylacrylamide and IL using ammonium persulphate as the initiator, to which were added already prepared Au NPs. These thermally sensitive composites formed, possessed reversible swelling/deswelling abilities in water, and demonstrated a reversible visible phase transition, which was detected by differential scanning calorimetric measurements. The lower critical solution temperature (LCST) showed dependency on the size of nanoparticles and the IL independently. It was seen that the LCST of PNIPAM-based composite films can be tuned from 32 °C to a range of 23-67 °C by choosing the desired Au NP size, its concentration and kind of IL.
More Related Videos
08:39Magnetic and Thermal-sensitive PolyN-isopropylacrylamide-based Microgels for Magnetically Triggered Controlled Release
Published on: July 4, 2017
09:02Using Polystyrene-block-polyacrylic acid-coated Metal Nanoparticles as Monomers for Their Homo- and Co-polymerization
Published on: July 9, 2015