Dataset and detailed methodology for structure and performance characterization of modified polymeric membranes

The data contained in this publication refers to protocols adopted characterization of clay nanoparticles (CN) membranes with and without the use of polyethylene oxide (PEO) as pore former. The membrane casting solutions were produced by dissolving PS (18% w/w) in NMP with addition of CN (1-5% w/w CN/PS) and/or PEO (1-5% w/w PEO/PS) when applicable. Membranes with no CN or PEO were used as a control. Pure water permeability of cast membranes was determined using the cross-flow cell unit. Viscosity was measured for most casting solution compositions and contact angle was measured for all membranes. The control membrane was further compared in detail to the highest permeability membranes with only CN (1.5%), only PEO (5%), 1.5% CN and 5% PEO (combination of optimal individual permeabilities), and 4.5% CN and 5% PEO (optimal combined permeability) regarding thickness, porosity, rejection, fouling resistance, surface charge, and thermal/mechanical properties. The relevance of the data presented here is to show details about methods for characterizing membranes for future comparison of performance and eventual improvement of characterization methods.