Study of the Fatigue Crack Growth in Long-Term Operated Mild Steel under Mixed-Mode (I + II, I + III) Loading

Grzegorz Lesiuk1, Michał Smolnicki1, Dariusz Rozumek2

  • 1Department of Mechanics, Material Science and Engineering, Wroclaw University of Science and Technology, Smoluchowskiego 25 Wrocław, PL-50372 Wrocław, Poland.

Materials (Basel, Switzerland)
|January 8, 2020
PubMed

Keywords:
crack closurecrack growth ratecrack pathsfatigue crack growthfinite element analysisfractographymixed-mode fracture

More Related Videos

Crack Monitoring in Resonance Fatigue Testing of Welded Specimens Using Digital Image Correlation05:30

Crack Monitoring in Resonance Fatigue Testing of Welded Specimens Using Digital Image Correlation

Published on: September 29, 2019

8.6K
Ultrasonic Fatigue Testing in the Tension-Compression Mode06:54

Ultrasonic Fatigue Testing in the Tension-Compression Mode

Published on: March 7, 2018

11.1K

Related Concept Videos

Fatigue01:21

Fatigue

Fatigue occurs when materials rupture under repeated or fluctuating loads, even at stress levels far below their static breaking strength. It typically results in brittle failure, even for ductile materials. It is a critical consideration in designing machines and structural components subjected to repetitive or varying loads. The nature of these loadings can range from fluctuating loads like unbalanced pump impellers causing vibrations to repeatedly bending a thin steel rod wire back and forth...
767
Fatigue Strength of Concrete01:22

Fatigue Strength of Concrete

Fatigue, in the context of materials science and engineering, refers to the weakening or failure of a material caused by repeatedly applied loads, even if these loads are below the strength limit of the material. Fatigue strength in concrete is a critical property that influences its durability and longevity. Concrete can fail in two ways due to fatigue. Static fatigue or creep rupture occurs under a constant load or one that increases slowly. The other failure mode is due to cyclical or...
481
Stress-Strain Diagram - Ductile Materials01:24

Stress-Strain Diagram - Ductile Materials

The stress-strain relationship in ductile materials such as structural steel or aluminium is intricate and progresses through several stages. When a specimen is loaded, it initially exhibits a linear length increase, depicted by a steep straight line on the stress-strain diagram. It indicates the material is elastically deforming and will return to its original shape once unloaded. However, when a critical stress value is reached, plastic deformation begins. This stage sees substantial...
1.8K
Stresses under Combined Loadings01:23

Stresses under Combined Loadings

When analyzing a bent tube with a circular cross-section subjected to multiple forces, it is crucial to determine the stress distribution in order to maintain structural integrity under varied load conditions.
The process begins by slicing the tube at critical points and analyzing the internal forces and stress components at these sections, focusing on the centroid. Normal stresses, generated by axial forces and bending moments, are either compressive or tensile and vary across the section from...
400
Mechanical Characteristics of Steel01:18

Mechanical Characteristics of Steel

The mechanical characteristics of steel are assessed through various tests that evaluate its strength, toughness, and flexibility. These tests include tension, torsion, impact, bending, and hardness assessments, each providing crucial information about steel's suitability for specific applications.
The tension test is fundamental for determining tensile strength. In this test, a steel specimen is stretched using a gripping device until it breaks. The data collected during this test are used...
978
Microcracking in Concrete01:20

Microcracking in Concrete

Microcracking in concrete refers to the tiny cracks that can form within the material even before any external load is applied. These microcracks typically occur at the interface between the coarse aggregate and the hydrated cement paste, often as a result of differential volume changes prompted by variations in stress-strain behavior, as well as thermal and moisture movement. Initially, these microcracks remain stable and do not grow substantially until the concrete is stressed to about 30...
383