Lightweight, Anisotropic, Compressible, and Thermally-Insulating Wood Aerogels with Aligned Cellulose Fibers

The growing demand for lightweight, renewable, and excellent thermal insulation materials has fueled a search for high performance biomass materials with good mechanical compressibility and ultralow thermal conductivity. We propose a fabrication method for making a lightweight, anisotropic, and compressible wood aerogel with aligned cellulose fibers by a simple chemical treatment. The wood aerogel was mainly composed of highly aligned cellulose fibers with a relative crystallinity of 77.1%. The aerogel exhibits a low density of 32.18 mg/cm³ and a high specific surface area of 31.68 m²/g due to the removal of lignin and hemicellulose from the wood. Moreover, the multilayer structure of the aerogel was formed under the restriction of wood rays. Combined with a nanoscale pore, the aerogel presents good compressibility and an ultralow thermal conductivity of 0.033 W/mK. These results show that the wood aerogel is a high quality biomass material with a potential function of thermal insulation through optimizing structures.