TEMPO-Oxidized Cellulose Cross-Linked with Branched Polyethyleneimine: Nanostructured Adsorbent Sponges for Water
Lucio Melone1,2,3, Bianca Rossi1,2, Nadia Pastori1,2
1Department of Chemistry, Materials, and Chemical Engineering "G. Natta", Politecnico di Milano, Piazza Leonardo da Vinci 32, 20133 Milano (Italy).
Abstract:
Adsorbent sponges for water remediation were prepared using TEMPO-oxidized cellulose nanofibers (TOCNFs) as three-dimensional scaffolds, and branched polyethyleneimine (bPEI, 25 KDa) as the cross-linking agent. TOCNFs were suspended in aqueous solution in the presence of variable amounts of bPEI. The mixtures were first freeze-dried and then thermally treated (from 60 to 102 °C over 10 h) promoting the formation of amide bonds between the carboxylic groups of TOCNF and the primary amines of bPEI. The resulting materials, which were characterized by FTIR and 13 C CP-MAS NMR spectroscopy, scanning electron microscopy, and elemental analysis, showed higher chemical and mechanical stability in water than non-reticulated cellulose composites. The high adsorption capability of the new sponges was verified for different organic pollutants (p-nitrophenol, 2,4,5-trichlorophenol, and amoxicillin), and heavy metal ion pollutants (Cu, Co, Ni, Cd), indicating their potential for water decontamination.