Characteristics and long-term effects of stabilized nanoscale ferrous sulfide immobilized hexavalent chromium in soil

Based on the phenomenon of soil polluted by Hexavalent chromium (Cr(VI)), this study systematically examined the efficiency, stability and feasibility of using sodium carboxymethyl cellulose-stabilized nanoscale ferrous sulfide (CMC-nFeS) to immobilize Cr(VI) in contaminated soil. The experiments described herein showed CMC-nFeS exhibited superior dispersity and a higher antioxidative effect than nFeS alone. Batch tests indicated the nanoparticles could effectively immobilize Cr(VI) in soil. At Cr(VI) concentrations of 56.01-502.21 mg/kg, the reducing capacity of CMC-nFeS was 54.68-198.74 mg Cr(VI)/g FeS. Following treatment with CMC-nFeS, the leachabilities of Cr(VI) and Cr_total determined by the Toxicity Characteristic Leaching Procedure (TCLP), Synthetic Precipitation Leaching Procedure (SPLP) and Physiologically Based Extraction Test (PBET) decreased significantly after 24 h and remained stable for 90 days. Column tests with water and simulated acid rain showed the injection of CMC-nFeS significantly increased the fixed Cr concentration and the procedure was environmentally friendly. Furthermore, analysis of the reaction mechanism demonstrated the best removal obtained in a neutral environment and Cr(VI) was reduced and immobilized in the form of Cr(OH)₃ and Fe_0.75Cr_0.25OOH confirmed by SEM-EDS and XPS analysis.