Use of solution-processed zinc oxide to prevent the breakdown in silver nanowire networks
Haoran Yu1,2, Ning Jin1, Zhenguo Wang2
1Key Laboratory of Electromagnetic Wave Information Technology and Metrology of Zhejiang Province, College of Information Engineering, China Jiliang University, Hangzhou, 310018, People's Republic of China.
Abstract:
The electrical breakdown is a bottleneck preventing AgNW networks from being used in high-current electronics such as transparent heaters or similar applications. The process of failure confirms that Joule-heating plays a key role in the formation of cracks perpendicular to the voltage direction. To improve the transfer of Joule heating, solution-processed ZnO nanoparticles were deposited on a gravure printed AgNW random network with good transparency. The AgNW-ZnO nanocomposites show better heating uniformity at higher temperatures because of their improved thermal conductivity. A 57.7% higher power density was obtained without failure, as well as the improved maximum average temperature rise from 72.2 °C to 97.9 °C, after the AgNW was composited with ZnO. This work opens up a new method to study AgNW failures for applications in high-current electronics.