Preparation of metal-organic framework based carbon materials and its application to adsorptive removal of cefepime...

Metal-organic framework based carbon material UC-X was prepared by template method, and adopted to remove cephalosporins from aqueous solution. The effect of templates including cetyltrimethyl ammonium bromide and sodium laurate was discussed. The UC-0.1 with the pore size of 5.38 nm has the best adsorption. According to FTIR spectrum, with the gradual increase of sodium laurate, the functional groups like CO increased, which promoted the adsorption capacity of cefepime in UC-X materials from 42.52 to 84.23 mg⋅g^-1. The optimal conditions for the adsorption of cefepime were determined by the response surface method: the adsorption temperature was 25.8 °C, the initial pH value was 6.11, and the ionic strength was 1.13 g·L^-1. Under the best adsorption condition, the adsorption-desorption experiments showed that the adsorption capacity of UC-0.1 material decreased by less than 10 % after five times usage, which indicated that its recycling property was competitive. The adsorption process conformed to the mixed-order kinetic model, and the error of equilibrium adsorption capacity between model fitting and actual experiments is not more than 1 %. The overall results of adsorption isotherm model and thermodynamic analysis demonstrated that Redlich-Peterson isothermal model could describe the adsorption process better.