The synthesis and characterization of Cu₂ZnSnS₄ thin films from melt reactions using xanthate precursors

Kesterite, Cu₂ZnSnS₄ (CZTS), is a promising absorber layer for use in photovoltaic cells. We report the use of copper, zinc and tin xanthates in melt reactions to produce Cu₂ZnSnS₄ (CZTS) thin films. The phase of the as-produced CZTS is dependent on decomposition temperature. X-ray diffraction patterns and Raman spectra show that films annealed between 375 and 475 °C are tetragonal, while at temperatures <375 °C hexagonal material was obtained. The electrical parameters of the CZTS films have also been determined. The conduction of all films was p-type, while the other parameters differ for the hexagonal and tetragonal materials: resistivity (27.1 vs 1.23 Ω cm), carrier concentration (2.65 × 10⁺¹⁵ vs 4.55 × 10⁺¹⁷ cm^-3) and mobility (87.1 vs 11.1 cm² V^-1 s^-1). The Hall coefficients were 2.36 × 10³ versus 13.7 cm³ C^-1.